Made in Japan, Production date - not defined , Best before - not defined
Rechargeable AA size battery.
Battery code: 1.2V 1900mAh HR6 AA BK-3MCCE Ni-MHNew battery voltage (no load applied) measured - 1.46V
Battery test was stopped once voltage (under constant 1000mA load) dropped to - 0.8V
During the test average battery temperature was 28.5C
Under load battery internal resistance measured at 30mOmh
Test parameter | Outcome |
---|---|
Current, mA | 1000 |
Capacity, mAh | 1891 |
Energy, Wh | 2.31 |
Duration, H:m:s | 1:53:43 |
New battery voltage (no load applied) measured - 1.44V
Battery test was stopped once voltage (under constant 500mA load) dropped to - 0.81V
During the test average battery temperature was 28.5C
Under load battery internal resistance measured at 34mOmh
Test parameter | Outcome |
---|---|
Current, mA | 500 |
Capacity, mAh | 1868 |
Energy, Wh | 2.3 |
Duration, H:m:s | 3:44:18 |
New battery voltage (no load applied) measured - 1.45V
Battery test was stopped once voltage (under constant 250mA load) dropped to - 0.8V
During the test average battery temperature was 27.5C
Under load battery internal resistance measured at 37mOmh
Test parameter | Outcome |
---|---|
Current, mA | 250 |
Capacity, mAh | 1899 |
Energy, Wh | 2.4 |
Duration, H:m:s | 7:36:0 |
New battery voltage (no load applied) measured - 1.44V
Battery test was stopped once voltage (under constant 50mA load) dropped to - 0.8V
During the test average battery temperature was 25.5C
Under load battery internal resistance measured at 31mOmh
Test parameter | Outcome |
---|---|
Current, mA | 50 |
Capacity, mAh | 1892 |
Energy, Wh | 2.4 |
Duration, H:m:s | 37:50:24 |
2018 (c) Battery.Reviews